| 品牌 | 帝人 |
| 貨號(hào) | PC |
| 用途 | 注塑 |
| 牌號(hào) | L-1225Z(100-K) |
| 型號(hào) | L-1225 |
| 品名 | PC |
| 外形尺寸 | 顆粒 |
| 生產(chǎn)企業(yè) | 帝人 |
| 是否進(jìn)口 | 是 |
產(chǎn)品參數(shù)
| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24hr，in 23℃ | ASTM D-570 | 0.20 | % | |
| 物理性能 | 阻燃性 | 厚度3.05mm | UL 94 | 94V-2 |
|
|
| 阻燃性 | 厚度1.47mm | UL 94 | 94V-2 |
|
||
| 透光率 | 厚度3mm | ASTM D-1003 | 88 | % | ||
| 比重 |
|
ASTM D-792 | 1.20 |
|
||
| 機(jī)械性能 | 拉伸模量 |
|
ASTM D-638 | 2170(22100) | Mpa(kgf/cm2) | |
| 洛氏硬度 |
|
ASTM D-785 | 77 | M標(biāo)度 | ||
| 彎曲模量 |
|
ASTM D-790 | 2280(23300) | Mpa(kgf/cm2) | ||
| 壓縮強(qiáng)度 |
|
ASTM D-695 | 77(790) | Mpa(kgf/cm2) | ||
| 拉伸率 | 屈服點(diǎn) |
|
ASTM D-638 | 6 |
|
|
| 斷裂點(diǎn) |
|
ASTM D-638 | 140 |
|
||
| 折射率 |
|
ASTM D-542 | 1.585 |
|
||
| 拉伸強(qiáng)度 | 屈服點(diǎn) |
|
ASTM D-638 | 63(640) | Mpa(kgf/cm2) | |
| 斷裂點(diǎn) |
|
ASTM D-638 | 74(750) | Mpa(kgf/cm2) | ||
| 耐沖擊強(qiáng)度值 | 艾氏、帶缺口厚度6.4mm | ASTM D-256 | 100(10) | j/m(kgf.cm/cm) | ||
| 耐沖擊強(qiáng)度值 | 艾氏、帶缺口厚度3.2mm | ASTM D-256 | 780(80) | j/m(kgf.cm/cm) | ||
| 彎曲強(qiáng)度 |
|
ASTM D-790 | 90(920) | Mpa(kgf/cm2) | ||
| 電氣性能 | 介電率 | 106Hz | ASTM D-150 | 2.9 |
|
|
| 介電正切 | 60Hz | ASTM D-150 | 0.0004 |
|
||
| 耐電弧性 |
|
ASTM D-495 | 110 | sec | ||
| 介電正切 | 106Hz | ASTM D-150 | 0.009 |
|
||
| 體積電阻率 |
|
ASTM D-257 | 3 | 1016Ω.cm | ||
| 介電率 | 60Hz | ASTM D-150 | 2.95 |
|
||
| 耐導(dǎo)電徑跡性（CTI） |
|
IEC 112 | 300 | V | ||
| 絕緣破壞強(qiáng)度 | 快速加壓值厚度1.6mm | ASTM D-149 | 30 | KV/mm | ||
| 加工性能 | 成型收縮率 | 流動(dòng)方向 |
|
ASTM D-955 | 0.5～0.7 | % |
| 垂直方向 |
|
ASTM D-955 | 0.5～0.7 | % | ||
| 熱性能 | 線膨脹系數(shù) | 流動(dòng)方向 |
|
ASTM D-696 | 7 | 10-5cm/cm/℃ |
| 垂直方向 |
|
ASTM D-696 | 7 | 10-5cm/cm/℃ | ||
| 負(fù)荷撓曲溫度 | 負(fù)荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 141 | °C | ||
| 溫度指數(shù) | 電學(xué)式 | 厚度1.47mm | UL 746B | 125 | °C | |
| 沖擊式 | 厚度1.47mm | UL 746B | 115 | °C | ||
| 非沖擊式 | 厚度1.47mm | UL 746B | 125 | °C | ||
| 負(fù)荷撓曲溫度 | 負(fù)荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 131 | °C | ||